Method for improving formed coke consolidation strength

A technology of consolidation strength and coke powder, which is applied in the field of coke preparation and can solve the problems of low strength of asphalt binder coke products

Active Publication Date: 2014-01-15
CENT SOUTH UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem of low strength of pitch binder coke products, the present invention aims to provide a method for increasing the strength of pitch binder coke

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1: The compressive strength of the carbonized coke obtained according to the process of Comparative Example 1 was 16.9 MPa by using superfine coke powder with an average particle size of 30.0 μm instead of fine coke powder with an average particle size of 500.0 μm.

Embodiment 2

[0013] Example 2: The compressive strength of the carbonized coke obtained according to the process of Comparative Example 1 was 19.3 MPa by using superfine coke powder with an average particle size of 8.6 μm instead of fine coke powder with an average particle size of 500.0 μm.

Embodiment 3

[0014] Example 3: The compressive strength of the carbonized coke obtained according to the process of Comparative Example 1 was 18.1 MPa by using superfine coke powder with an average particle size of 4.5 μm instead of fine coke powder with an average particle size of 500.0 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving formed coke consolidation strength. Superfine grinding fillers (the superfine grinding fillers are coke powder or anthracite, and the average particle size of the fillers is less than 30.0 micrometers) are mixed with pitch, and then evenly mixed with the coke powder to obtain a mixture, the obtained mixture is added with water for wetting and then fully and evenly mixed again, and is subjected to pressing and forming process as well as volatilization and carbonization treatment at normal temperature to obtain carbonized formed coke, wherein the compression strength can be up to above 19.0 MPa. According to the method disclosed by the invention, the superfine grinding fillers are added into the pitch, enables the superfine grinding fillers to be embedded in a skeleton structure formed by carbonized pitch so as to fill pores created in coal tar pitch heat treatment, enrich the carbonized skeleton and enhance a bridge chain effect among coke powder particles and further improve the formed coke strength. According to the method, only a procedure of superfine grinding filler preparation needs to be added in the method, so that the effect of obvious improvement of the formed coke strength can be reached by performing the process in the conventional formed coke production process.

Description

technical field [0001] The invention belongs to the technical field of coke powder molding, and relates to a technology and method for preparing coke with asphalt as a binder, in particular to a coke preparation technology for adding superfine grinding fillers to asphalt as skeleton fillers to improve the consolidation strength of asphalt binders and methods. Background technique [0002] Coke is the main fuel in chemical industry, metallurgy, calcium carbide and other industries. It is required to have a certain lumpiness when used, but coke powder is inevitably produced during coke transportation or crushing. Coke powder is used as cheap ordinary fuel or even discarded because of its small particle size (generally below 10mm) and does not meet the requirements of the production process. At present, coke users lack effective recycling technology for it. A large amount of coke powder is processed cheaply, which not only causes a huge waste of coke resources, but also the op...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10L5/16
Inventor 杨永斌姜涛李骞钟强郭宇峰李光辉范晓慧黄柱成白国华郑琼香陈丽娟
Owner CENT SOUTH UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com