Preparation method of iron-based nanocrystal spectroscopic standard sample
A technology for iron-based nanocrystals and spectral standard samples, which is applied in the field of preparation of iron-based nanocrystals spectral standard samples, can solve the problems of difficulty, few iron-based nanocrystalline standard samples, and large component segregation of samples, and achieves accurate effect of data
Active Publication Date: 2016-01-20
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF8 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] In order to improve the stability of product performance, its composition consistency is very important. At present, spectrometers are commonly used to detect the composition of iron-based nanocrystals, but spectrometers need qualified standard samples to detect reasonable composition values. Iron-based nanocrystalline alloy standard samples are due to their alloy There are many elements, and the smelting is difficult. So far, no national standard material has been formed, and there are few ideal iron-based nanocrystalline standard samples in actual use. There is Nb element with a high melting point in the alloy composition, which is easy to burn out The B element and the easily oxidizable Si element bring greater difficulty to the design of the smelting process, and the traditional sampling method will lead to the formation of pores and cracks in the sample block. Low, large component segregation between samples, which has higher requirements for the production of iron-based nanocrystalline spectral standards
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] The technical solutions of the present invention will be described in further detail below with reference to the accompanying drawings and embodiments.
[0018] The preparation method of the iron-based nano crystal spectrum standard sample provided by the invention provides guarantee for the development and production of the iron-based nano crystal material.
[0019] figure 1 It is a flowchart of the iron-based nanocrystal spectral standard sample preparation method of the present invention, as shown in the figure, the method includes:
[0020] Step 101, using the iron element as the base, select the chemical formula of the standard sample ratio and calculate the raw material addition ratio; the added raw materials include industrial pure iron, ferro-boron fragments, ferro-niobium fragments, silicon fragments, and electrolytic copper.
[0021] Specifically, taking iron as the base, silicon, boron, niobium and copper as the high and low standards, distributed in steps, ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a preparation method of a standard spectrum sample of Fe-based nanocrystalline. The method comprises the following steps: a chemical formula of a standard sample ratio is selected, and a raw material adding ratio is calculated; raw materials are added in a vacuum induction furnace according to the ratio, and the vacuum induction furnace is adopted to smelt the raw materials into molten steel; the molten steel is poured in a cylindrical graphite mold for heat treatment and forms steel samples; the steel samples are subjected to linear cutting, grinding and polishing treatment, and qualified steel samples are selected according to microscopic examination and ultrasonic nondestructive inspection; the qualified steel samples are subjected to uniformity analysis; a detection result is analyzed, and an average value is taken as an fixed value of the elements; and the standard sample is formed. The invention provides one preparation method of the standard spectrum sample of the Fe-based nanocrystalline by starting from chemical component design, a smelting process and a final sample processing process, a prepared product can be excited effectively and uniformly by a spectrometer, so that more accurate data are obtained, and guarantee is provided for development and production of a Fe-based nanocrystalline material.
Description
technical field [0001] The invention relates to a preparation method of a spectral standard sample, in particular to a preparation method of an iron-based nanocrystal spectral standard sample. Background technique [0002] The iron-based nanocrystalline alloy is mainly composed of Fe elements, and a small amount of Nb, Cu, Si, and B elements are added to form an alloy. After rapid solidification, an amorphous material is formed. After heat treatment, microcrystals with a diameter of 10-20nm are obtained. Distributed on an amorphous substrate, it is called iron-based nanocrystalline and iron-based ultrafine crystal materials. Due to its specific structure, it has a wide range of applications. [0003] In order to improve the stability of product performance, its composition consistency is very important. At present, spectrometers are commonly used to detect the composition of iron-based nanocrystals, but spectrometers need qualified standard samples to detect reasonable comp...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): G01N1/28
Inventor 尹丽娟王宏鉴刘红玉周立伟
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Features
- R&D
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
Why Patsnap Eureka
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com