Fine crystal non-quenched and tempered steel for connecting rod

A non-quenched and tempered steel, fine-grained technology, applied in the field of fine-grained non-quenched and tempered steel and micro-alloyed non-quenched and tempered steel, can solve the problems of weakening the economy, affecting the fatigue performance of parts, and ductile fracture in the ferrite region.

Inactive Publication Date: 2015-05-20
SHANGHAI UNIV
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the good toughness of the ferrite in the traditional ferrite + pearlite structure, the ferrite region at the root of the notch is prone to ductile fracture, resulting in poor bursting properties
In recent years, the research and development of related materials has also been carried out in China. The most typical one is a non-quenched and tempered steel for medium-carbon expansion connecting rods, which has good expansion properties, but due to the addition of up to 0.25% of microalloying elements V , the cost of steel increases, which weakens the economy of the steel; at the same time, too high Si content (2%) also deteriorates the surface quality of the forging and affects the fatigue performance of the part; in addition, in order to improve the machinability, the steel is added The harmful element Pb of about 0.1% is not conducive to environmental protection, which limits the application of the steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fine crystal non-quenched and tempered steel for connecting rod
  • Fine crystal non-quenched and tempered steel for connecting rod
  • Fine crystal non-quenched and tempered steel for connecting rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] According to the chemical composition range of the above design: three furnaces of the steel of the present invention and one furnace of comparative steel were melted on the high vacuum non-consumable arc melting equipment. The chemical composition of Invention Steel 1 is: (Ti+Nb) 0.1%, C 0.3%, Si 0.60%, Mn 0.75%, P 0.08%, S 0.05%, Cr 0.10%, V 0.05%, B 0.0005%, Fe quantity. The chemical composition of Invention Steel 2 is: (Ti+Nb) 0.15%, C 0.40%, Si 0.65%, Mn 0.80%, P 0.09%, S 0.06%, Cr 0.15%, V 0.15%, B 0.0007%, Fe quantity. The chemical composition of Invention Steel 3 is: (Ti+Nb) 0.20%, C 0.45%, Si 0.70%, Mn 0.9%, P 0.10%, S 0.07%, Cr 0.20%, V 0.25%, B 0.001%, Fe quantity. The chemical composition of the comparison steel is: C 0.72%, Si 0.32%, Mn 0.57%, P 0.02%, S 0.06%, Cr 0.17%, V 0.03%, Fe balance.

[0024] With the help of J-MatPro thermodynamic software, the phase diagram and CCT curve (continuous cooling transformation curve of supercooled austenite) of ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses fine crystal non-quenched and tempered steel for a connecting rod and belongs to the technical field of special alloy steel. The fine crystal non-quenched and tempered steel is characterized by being prepared from the following elements in percentage by weight: 0.10-0.20% of (Ti+Nb), 0.35-0.45% of C, 0.60-0.70% of Si, 0.75-0.9% of Mn, 0.08-0.10% of P, 0.05-0.07% of S, 0.10-0.20% of Cr, 0.05-0.25% of V, 0.0005-0.001% of B and the balance of Fe. The metallographic structure of the alloy steel is upper bainite. On the premise that the expansion fatigue property of the connecting rod is ensured, the alloy steel is good in cutting processing property and expansion property.

Description

technical field [0001] The invention relates to a micro-alloyed non-quenched and tempered steel, and in particular provides a fine-grained non-quenched and tempered steel used for connecting rods, which has good cutting performance and good swelling performance on the premise of ensuring the fatigue performance of the connecting rod when it expands. break performance. The invention belongs to the field of special alloy steel. Background technique [0002] The connecting rod of automobile engine is an important part of the engine. It bears the effect of cyclic stress in the working process, and its failure mode is mainly fatigue damage, so the fatigue performance directly affects the application range of the connecting rod. The performance stability of the engine requires that the connecting rod should have high stiffness and fatigue strength. Due to the complex traditional machining process and high precision requirements, especially the big head hole of the connecting rod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/60
CPCC22C38/60C22C38/02C22C38/04C22C38/12C22C38/18C22C38/32
Inventor 王晓吴俊玮夏书文殷星河韦习成王武荣
Owner SHANGHAI UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com