Diamond glaze for ceramic tiles

[0015] 1) Formula in weight percentage:

[0016] Spodumene powder 40%, frit powder 10%, potash feldspar powder 10%, burnt talc powder 5%, barium carbonate powder 8%, wollastonite powder 10%, kaolin powder 5%, white corundum powder 1%, zinc oxide 5 %,

[0017] Two) Preparation method:

[0018] Step 1. First prepare the frit powder. The formula for the weight percentage of the frit powder is as follows: potassium feldspar 30%, wollastonite 4%, raw talc 5%, barium carbonate 5%, calcite 16%, quartz 20%, coarse oxidation Aluminum 10%, 95 zinc oxide 2%, potassium carbonate 1%, strontium carbonate 1%,

[0019] Preparation of frit powder:

[0020] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0021] 2) After the frit is taken out and cooled to room temperature, it is crushed with a pulverizer, and then sieved with a 100-mesh sieve for use. If it is unqualified, it is crushed and sieved to pass;

[0022] Step 2. Put all the formula materials in a) we...

[0024] 1) Formula of weight percentage:

[0025] Spodumene powder 27%, frit powder 13%, potash feldspar powder 13%, burnt talc powder 10%, barium carbonate powder 12%, wollastonite powder 13%, kaolin powder 7%, white corundum powder 3%, zinc oxide 6 %,

[0026] Two) Preparation method:

[0027] Step 1. First prepare the frit powder. The formula of the frit powder is as follows: 25% potash feldspar, 5% wollastonite, 6% raw talc, 7% barium carbonate, 18% calcite, 21% quartz, and coarse oxidation Aluminum 12%, 95 zinc oxide 3%, potassium carbonate 2%, strontium carbonate 1.5%,

[0028] Preparation of frit powder:

[0029] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0030] 2) After the frit is taken out and cooled to room temperature, it is crushed with a crusher, and then sieved with a 100-mesh screen for use. If it is unqualified, it is crushed and sieved to pass;

[0031] Step 2. Put all the formula materials in a) weight percentage into a ...

[0033] 1) Formula in weight percentage:

[0034] Spodumene powder 15%, frit powder 15%, potash feldspar powder 15%, burnt talc powder 15%, barium carbonate powder 15%, wollastonite powder 15%, kaolin powder 8%, white corundum powder 5%, zinc oxide 7 %,

[0035] Two) Preparation method:

[0036] Step 1. First prepare the frit powder. The formula for the weight percentage of the frit powder is as follows: potassium feldspar 20%, wollastonite 6%, raw talc 8%, barium carbonate 8%, calcite 20%, quartz 22%, coarse oxidation Aluminum 14%, 95 zinc oxide 4%, potassium carbonate 3%, strontium carbonate 2%,

[0037] Preparation of frit powder:

[0038] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0039] 2) After the frit is taken out and cooled to room temperature, it is crushed with a crusher, and then sieved with a 100-mesh screen for use. If it is unqualified, it is crushed and sieved to pass;

[0040] Step 2. Put all the formula materials in a) we...