A kind of polyester film for optical high permeability glue protection and preparation method thereof

A technology of polyester film and high-permeable adhesive, applied in the field of polyester film, can solve the problems of high surface roughness, high cost, and inability to remove defects, etc., and achieve substantial characteristics, excellent temperature resistance, and excellent products performance effect

Active Publication Date: 2019-05-17
ZHEJIANG QIANGMENG IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The polyester film for optical high-transparency protection requires few internal and external defects, high surface smoothness, high haze, and high light transmittance; the current existing biaxially stretched polyester film production line and raw material formula are difficult to achieve the above-mentioned Technical requirements; one is that during the production process of the film, static electricity will absorb the particle powder layer in the air and form impurities inside the film, which need to be removed by high-precision filters, which is very costly, and it is difficult to remove the defects inside and outside the film Clean, the remaining impurities have the function of removing gel, so that the defects inside and outside the film cannot be removed, and the anti-blocking agent used in the prior art will make the surface roughness of the film relatively high, which will eventually cause defects on the surface of the optical high-transparency adhesive film , if it is used in optical components, it will affect the performance of optical components; and the polyester protective film used for the protection of ordinary release optical glue used in industrial products in the market currently relies on foreign imports, and foreign production processes are protected as trade secrets and have not been disclosed. , and the defects inside and outside the film of the produced product are relatively large, the defects above 200 microns are more than 50 per square meter, and the surface roughness of the film is generally Ra>0.06

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyester film for optical high permeability glue protection and preparation method thereof
  • A kind of polyester film for optical high permeability glue protection and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] like figure 1 Shown, a kind of polyester film for optical high permeable glue protection, comprises the first base material layer 1, the second base material layer 2, intermediate core layer 3, the thickness of intermediate core layer 3 occupies 10% of the polyester film for optical high permeable adhesive protection. 60%-80% of the total thickness of the film, the first base material layer 1 and the second base material layer 2 respectively account for 10%-20% of the total thickness of the polyester film for optical high-permeability adhesive protection.

[0035] Wherein the middle core layer 3 is a polyester chip with a material purity of 99%-100%. The material composition of the first substrate layer 1 and the second substrate layer 2 is: 50%-70% nano-scale masterbatch MB10, 3%-5% nano-scale antistatic additive masterbatch ATS10, 47%-25% polyester Sliced; nano-grade MB10 masterbatch is made of 0.1%-1.2% nano-grade silica, 0.01%-0.1% particle size 1.0 micron-1.8 micr...

Embodiment 2

[0037] like figure 1 Shown, a kind of polyester film for optical high permeable glue protection, comprises the first base material layer 1, the second base material layer 2, intermediate core layer 3, the thickness of intermediate core layer 3 occupies 10% of the polyester film for optical high permeable adhesive protection. 65%-75% of the total thickness of the film, the first base material layer 1 and the second base material layer 2 respectively account for 12.5%-17.5% of the total thickness of the polyester film for optical high-permeability adhesive protection.

[0038]Wherein the middle core layer 3 is a polyester chip with a material purity of 99%-100%. The material composition of the first substrate layer 1 and the second substrate layer 2 is: 55%-65% nano-scale masterbatch MB10, 3%-5% nano-scale antistatic additive masterbatch ATS10, 30%-45% polyester Sliced; nano-grade MB10 masterbatch is made of 0.1%-1.2% nano-grade silica, 0.01%-0.1% particle size 1.0 micron-1.8 m...

Embodiment 3

[0040] like figure 1 Shown, a kind of polyester film for optical high permeable glue protection, comprises the first base material layer 1, the second base material layer 2, intermediate core layer 3, the thickness of intermediate core layer 3 occupies 10% of the polyester film for optical high permeable adhesive protection. 80% of the total thickness of the film, the first substrate layer 1 and the second substrate layer 2 respectively account for 10% of the total thickness of the polyester film for optical high-permeable adhesive protection.

[0041] Wherein the middle core layer 3 is a polyester chip with a material purity of 99.8%. The material composition of the first substrate layer 1 and the second substrate layer 2 is: 70% nanoscale masterbatch MB10, 4% nanoscale antistatic additive masterbatch ATS10, 26% polyester chip; nanoscale MB10 masterbatch is made of 1% nano-scale silica, 0.05% particle size 1.0 micron-1.8 micron silica, 0.05% kaolin, 0.5% silane coupling agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of polyester films, and discloses a polyester film used for protecting optical high-transmittance adhesive and a preparation method of the polyester film. The polyester film used for protecting the optical high-transmittance adhesive comprises a first base material layer (1), a second base material layer (2) and a middle core layer (3). The preparation method of the polyester film used for protecting the optical high-transmittance adhesive comprises mixing silicon dioxide, a silane coupling agent and bottle grade polyester chips to prepare MB10 master batches, mixing a nanometer ITO antistatic agent and bottle grade polyester chips to prepare ATS 10 antistatic master batches, and performing material feeding, crystallization, drying, melting by an extruder, sheet casting, longitudinal stretch, transverse stretch, moulding, pulling, corona processing and winding of a three-layer co-extrusion BOPET production line to obtain the polyester film used for protecting the optical high-transmittance adhesive provided by the invention. The film is in a clean shop during the whole production process. The technical scheme disclosed by the invention can effectively reduce inner and outer defects of the polyester film used for protecting the optical high-transmittance adhesive, and increase the smooth, clean and flat degrees of the film surfaces.

Description

technical field [0001] The invention relates to the field of polyester films, in particular to a polyester film for optical high-permeability adhesive protection and a preparation method thereof. Background technique [0002] The polyester film for optical adhesive protection belongs to the high-end release film and protective film in the fields of electronics and optics; when the optical high-transparency adhesive is formed, the film is used as the base material, and after the optical high-transparency adhesive is formed, the film is used as Protective film, this film is used as a release film when optically transparent adhesive is used. [0003] The polyester film for optical high-transparency protection requires few internal and external defects, high surface smoothness, high haze, and high light transmittance; the current existing biaxially stretched polyester film production line and raw material formula are difficult to achieve the above-mentioned Technical requiremen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/20B32B27/36B32B33/00B29C48/18B29C69/02B29L7/00B29L9/00
CPCB29C48/0018B29C48/08B29C48/21B29L2007/00B29L2009/00B32B27/08B32B27/20B32B27/36B32B33/00B32B2250/24B32B2307/306B32B2307/412B32B2307/54
Inventor 易志龙胡培隆
Owner ZHEJIANG QIANGMENG IND
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com