Pearlitic steel rail with high strength and toughness and producing method thereof

Inactive Publication Date: 2016-03-03
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0008]The present invention further provides a pearlitic steel rail with hi

Problems solved by technology

However, improved strength and hardness of pearlitic steel rails will result in further degraded toughness and plasticity that are low originally.
Consequently, the development of pearli

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test
No Example Login to View More

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Login to View More

Abstract

A pearlitic steel rail with high strength and toughness and a producing method thereof. The producing method comprises: controlling the following processing conditions in a rolling procedure to produce the pearlitic steel rail with high strength and toughness: initial rolling temperature of 1,120-1,180° C., final rolling temperature of 840-880° C., rail profile reduction in last two rolling passes of 6%-12%; the steel rail is cooled to 600° C. or lower at a cooling rate ≦2.0° C./s after final rolling, and then air-cooled to room temperature; the chemical composition of the steel rail meets the following requirements: C: 0.75%-0.84%, Si: 0.30%-0.80%, Mn: 0.50%-1.50%, V: 0.04%-0.12%, Ti: 0.004%-0.02%, and 0.10%≦V+10Ti≦0.25%, [N]≦30 ppm, P≦0.020%, S≦0.008%, with the remaining content consisting of Fe and inevitable impurities.

Description

CROSS REFERENCE TO RELATED APPLICATIONS[0001]This application claims priority to Chinese Application No. 201410443977.0, filed on Sep. 2, 2014, entitled “Pearlitic Steel Rail with High Strength and Toughness and Producing Method Thereof”, which is specifically and entirely incorporated by reference.FIELD OF INVENTION[0002]The present invention relates to a steel rail, in particular to a pearlitic steel rail with high strength and toughness and a producing method thereof.BACKGROUND OF THE INVENTION[0003]The rapid development of railroads has raised higher requirements for the service performance of steel rails. Especially, for heavy-duty railroads with high traffic volume and high axle load, the early replacement of steel rails as a consequence of quick wearing has become a major factor that has impacts on the efficiency of railroad transportation. Usually, alloying, heat treatment or a combination of them is utilized in the production of steel rails, in order to improve the overall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C21D6/00C21D8/00C21D9/04C22C38/02C22C38/04C22C38/12
CPCC22C38/12C22C38/04C22C38/02C21D6/008C21D8/005C21D9/04C21D6/005C22C38/14C21D1/19C21D1/84C21D2211/009
Inventor HAN, ZHENYUZOU, MINGTAO, GONGMINGGUO, HUALI, DADONGDENG, YONG
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com